deoxidizing

英

美

网络  脱氧; 去氧

医学

双语例句

• The size of deoxidizing products increases with the increased degree of supersaturation of deoxidizing elements;
  脱氧产物尺寸随脱氧元素过饱和度增加而增加；
• Titanium powders produced by deoxidizing TiO2 directly is the mainstream, if we can empolder a kind of more simple and lower cost method to produce Titanium powders, it will certainly stimulate the development of Titanium production industry.
  采用TiO2直接还原法生产钛粉已经成为生产钛粉的主要研究方法，如果能开发出更简单、成本更低的方法必将极大地促进钛粉生产行业的发展。
• The preparation of ultrafine WO_3 powders and the deoxidizing and carbonizing of WO_3 to WC were studied. Well abrasive resistant metal composite coating strengthened by ultrafine WC particles was prepared by flame thermal spray method and abrasive wear property was studied.
  本文探索了超细WO3粉的制备及其还原碳化为WC粉的方法，采用火焰热喷涂工艺，制备了耐磨性能较好的超细WC陶瓷&金属复合涂层，并研究了涂层的耐磨性能。
• The analytic results have shown that the new magnesium reduction process deoxidizing by liquid calcium is feasible.
  结果表明，以液态钙为还原剂的还原工艺是可行的。
• Control model of deoxidizing and alloying for steelmaking process
  炼钢过程的脱氧合金化控制模型
• Metallurgical Problems in Heat-Resistance Steel Composition Design of Deoxidizing Ladle for Refining Mg
  炼镁还原罐用耐热钢成份设计中的金属学问题
• Preparation of high-concentration sulfur dioxide from deoxidizing phosphogypsum with compound reducing agent
  硫脲作还原剂制备二氧化锰及其电化学性能复合还原剂还原分解磷石膏制取高浓度二氧化硫
• The technology of aluminium deoxidizing and alloying has been studied. That is, after preliminary argon blowing and oxygen detecting for the aluminum containing steel, determine the feeding amount of aluminium according to the oxygen content in steel and then reblow argon.
  对含铝钢经预吹氩定氧后，根据钢中氧含量确定加铝量，再补吹氩的铝脱氧合金化工艺进行研究和探索。
• The composition of the secondly and thirdly deoxidizing products can be controlled through controlling the content of aluminum and calcium of the strong deoxidizing elements, making them have good distortion ability in hot work.
  二次和三次脱氧产物的成分可以通过控制钢液中强脱氧元素铝和钙的含量来控制，使它们具有良好的热加工变形能力。
• Third the influence of the liquid steel flowing on the eliminating of firstly deoxidizing products is studied;
  研究了钢液流动现象对一次脱氧去除的影响；